microflaw

英

美

【化】显微裂纹

The results show that in the initial stage of micro-arc oxidation the obtained ceramic coating is compact and nearly no microflaw can be observed, the microflaws like holes begin to appear in the exterior and finally irregular holes fill with 90% of the thickness range.
结果表明：微弧氧化初期，陶瓷层致密，几乎观察不到显微缺陷，随着处理时间的延长及陶瓷层的增厚，其外侧开始出现孔洞类缺陷，直至90%厚度范围布满相互交错的不规则孔洞；
The change regulation of microflaw and phases constitution in the process of growth of ceramic coating formed by micro-arc oxidation on magnesium alloys and their influence on corrosion-resistance were studied by SEM, XRD and salt spray tests.
利用SEM，XRD及盐雾腐蚀等试验手段，研究了MB8镁合金微弧氧化陶瓷层生长过程中显微缺陷与相组成的变化规律及其对耐蚀性的影响。
Due to microflaw presence in the area affected by welding, there is a greater difference between the actural strength analysis and life evaluation and these done by the traditional method. It seems that the analysis and evaluation made based on fracture theory are much more acceptable.
由于焊接影响区微裂纹的存在，对其强度分析和寿命估算的传统方法有时与实际情况相差较大，而基于断裂理论的强度分析和寿命估算方法则更为可靠。